Longkou Aoxing Insulating Material Co.,Ltd

 
  • phenolic cloth rod
    Type Diameter
    (mm) Density (g/cm3) Flexural strength (Mpa) Compressive
    Strength
    (Mpa) Breakdown vottage parallel(kv)
    3722-1 6-100 1.28 88.24 104.8 N/A
    3722 6-100 1.28 110.3 131.0 N/A
  • epoxy glass molded rod
    Type Diameter
    (mm) Density (g/cm3) Flexural strength (Mpa) Compressive
    Strength
    (Mpa) Breakdown vottage parallel(kv)
    3841 6-50 1.70 241.3 241.3 15
  • phenolic cellulose paper base laminated sheet
    1.Flexural strength perpendicular to laminations 120Mpa min
    pression strength vertical 120 Mpa min
    3.Tensile strength 250 Mpa min
    4.Bonding strength 3200
    5.Density 1.3-1.45 g/cm3
  • phenolic cotton cloth laminated sheet
    1.Flexural strength perpendicular to laminations 100Mpa min2.Impact strength parallel to laminations 8.8 KJ/m2min3.Tensile strength 80 Mpa min4.Breakdown voltage parallel to laminations(90 degree in
  • epoxy glass fabric laminated sheet
    1.Flexural strength perpendicular to laminations 340 Mpa min2.Impact strength parallel to laminations 33 KJ/m2minpression strength vertical 350 Mpa min4.Tensile strength 300Mpa min5.Dielectric
 