1. The products are featured by high hardness, big density, low wear lost, good normalization, good corrosion-resistance, etc. It is the most ideal high-efficient grinding medium for milling equipment.
Low wear rate with high quality of China raw Alumina powder of less than 1μm of Ultimate crystal size.
Valuable test results for the customers through different test methods according to customers equipments and use conditions.
Best appearance and varied sizes at will by advanced machine rolling processing.
Continual steady quality by automatic equipments to control the quantity of the powder and water.
Fine crystal size to be controlled in 90 meters long tunnel kiln with 1500 broad firing section.
2.Performance Index of Microlite Abrasive Alumina Arc lining plate/tile
|
Product
Performance Index |
92
92 Series |
95
95 Series |
|
Al2O3 (%) |
≥92 |
≥95 |
|
Mohs Hardness |
9 |
9 |
|
Water Absorption(%) |
0.02 |
0.02 |
|
(Mpa)
Fracture Toughness |
3.65 |
3.75 |
|
Mpa
Bending Strength |
255 |
275 |
|
(g/cm3)
Bulk Density |
≥3.60 |
≥3.65 |
3. Specification of Microlite Wear-resisting Alumina Lining Plate, Pieces
|
Name |
L(mm)
Length |
W(mm)
Width |
H(mm)
Height |
Remark |
|
10×10
10×10 Lining Pieces |
10 |
10 |
410 |
Can be stuck to a sheet |
|
17.5×17.5
17.5×17.5 Lining Pieces |
17 |
17 |
410 |
Can be stuck to a sheet |
|
20×20
20×20 Lining Pieces |
20 |
20 |
410 |
Can be stuck to a sheet |
|
120×80 |
120 |
80 |
1020 |
Wear-resisting Perforated or Non-perforated Lining Board |
|
110×37/34×12 |
110 |
37/34 |
12 |
Wear-resisting Pipe TrapezoidLining Board |
|
130×50/47×12 |
130 |
50(47) |
12 |
Wear-resisting Pipe TrapezoidLining Board |
|
150×100 |
150 |
100 |
1025.4 |
Wear-resisting Perforated or Plain Lining Board |
|
150×60/57 |
150 |
60/57 |
10/12 |
Wear-resisting Pipe TrapezoidLining Board |
|
100×81.6/78.5×20 |
100 |
81.6/78.5 |
20 |
Wear-resisting Arc Lining Board |
4.The microlite alumina wear-resisting lining plate and slice takes alumina as the main material, adds metal oxide as the flux, makes the powder granularity in 1μm~2μm, through dry-compacted and burned with the 1500 temperature to be special type wear-resisting ceramic.
5. Its rockwell hardness is HRA80-90 which is only inferior to the diamond. The wear-resisting performance is far beyond that of steel and the stainless steel.
6. Characteristics of wear-resisting, anti-impact and easy construction, etc. which is ideal surface wear-resisting material for material transporting and powder selecting equipment of steel plant, thermal power plant, cement and mine.
7. Its theoretic wear-resistance is equal to 260 times of manganese steel, 170 times of chrome steel. After actually surveying, it can effectively increase the service life of equipment more than 10 times.
8. Density is 3.55g/cm3, only half of the steels density,to reduce the equipment load greatly, save the use cost of equipment.