Steel Cut Wire Shot

Specifications

Steel cut wire shot
Main specification: 1.0mm,1.5mm,2.0mm,2.5mm
Chemical composition: C 0.45-0.75%, Mn 0.40-1.20%, Si 0.10-0.30%, S ≦0.04%, P ≦0.04%
Hardness: 1.0mm 51-53 HRC; 1.5mm 41-45 HRC
Durability: 3000-3500 Times
Microstructure: Deformed Pearlite
Density: 7.8g/cm3
 
Products Cut Wire Shot   
　  C 0.45～0.75%   
  Mn 0.40～1.20%   
  Si 0.10～0.30%   
  S ＜0.04%    
  P ＜0.04%    
Microhardness 1.0mm: 51～53 HRC(525～561HV)
1.5mm: 41～45 HRC(388～436HV)   
Hardness Deviation Max Deviation ±1.0HRC or ±40HV   
Tensile Intensity 1.0mm: 1750～2150 Mpa
1.5mm: 1250～1450 Mpa   
Microstructure      
portrait             Landscape
even deformed perlite   
Density 7.8g/cm3 
Shandong Kaitai Industrial Technologies Co., Ltd is the biggest manufacture of metal abrasive in China which integrates with technical research, development and production. The main products are:
Cast Steel Shot (S70,S110,S170,S230,S280,S330,S390,S460,S550,S660,S780,S930)
Cast Steel Grit (G10, G12, G14, G16, G18, G25, G40, G50, G80)
Stainless Steel Shot (316,304,301,202,205,430,410)
Steel Cut Wire Shot (CW1.0, CW1.5, CW2.0, CW2.5)
Aluminum Shot (0.6mm, 0.8mm, 1.0mm, 1.2mm, 1.5mm, 2.0mm)
Copper Shot (0.6mm, 0.8mm, 1.0mm, 1.2mm, 1.5mm, 2.0mm)
Zinc Shot (0.6, 0.8, 1.0, 1.2, 1.5, 2.0)              
Stainless Steel Wire (410,430,205,202,201,304,316)
High Carbon Steel Cut Wire Shot
Shot Blasting Machine and Wearable Spare parts